高丽飞,杜敏.2205双相不锈钢在淡化海水中的点蚀行为[J].装备环境工程,2017,14(2):11-18. GAO Li-fei,DU Min.Pitting Corrosion Behaviors of 2205 Duplex Stainless Steel in Desalination Seawater[J].Equipment Environmental Engineering,2017,14(2):11-18. |
2205双相不锈钢在淡化海水中的点蚀行为 |
Pitting Corrosion Behaviors of 2205 Duplex Stainless Steel in Desalination Seawater |
投稿时间:2016-12-16 修订日期:2017-02-15 |
DOI:10.7643/ issn.1672-9242.2017.02.003 |
中文关键词: 不锈钢 反渗透 点蚀 淡化海水 |
英文关键词:stainless steel reverse osmosis pitting corrosion desalination seawater |
基金项目:国家自然科学基金(41576076);国家重点基础研究发展计划(973计划, 2014CB643300) |
|
Author | Institution |
GAO Li-fei | 1.College of Chemical Engineering, Ocean University of China, Qingdao 266100, China;2.Key Laboratory of Marine Chemistry Theory and Technology, Ministry of China, Qingdao 266100, China |
DU Min | 1.College of Chemical Engineering, Ocean University of China, Qingdao 266100, China;2.Key Laboratory of Marine Chemistry Theory and Technology, Ministry of China, Qingdao 266100, China |
|
摘要点击次数: |
全文下载次数: |
中文摘要: |
目的 研究2205双相不锈钢在一级反渗透(RO)淡化海水、海水及浓缩海水中的点蚀行为。方法 运用开路电位、交流阻抗、阳极极化曲线和电化学频率调制技术研究2205双相不锈钢在不同温度(60~90 ℃)及不同海水(一级反渗透淡化海水、天然海水、1.6倍浓缩海水)中的点蚀行为。结果 2205双相不锈钢在一级RO淡化海水中,随温度升高,自腐蚀电位逐渐负移。在80 ℃的一级RO淡化海水中,在浸泡1 d时即有发生点蚀的倾向,在第28 d时已经发生了稳态蚀点。浸泡初期不锈钢的扰动电流为2 µA/cm2之内,浸泡41 d的扰动电流接近12 µA/cm2,且其值波动幅度更大。结论 随着温度的升高钝化膜稳定性降低,2205不锈钢耐蚀性降低。钝化状态下,其在一级RO淡化海水中比在海水中腐蚀严重,点蚀敏感性随Cl–浓度的升高而增加。 |
英文摘要: |
1.College of Chemical Engineering, Ocean University of China, Qingdao 266100, China;2.Key Laboratory of Marine Chemistry Theory and Technology, Ministry of China, Qingdao 266100, China |