李亨特,刘星辰,荆江平,孙萌萌,陈卓元,孙明先,侯健.制备方法对二氧化钛粉末薄膜光电极性能的影响研究[J].装备环境工程,2017,14(6):17-21. LI Heng-te,LIU Xing-chen,JING Jiang-ping,SUN Meng-meng,CHEN Zhuo-yuan,SUN Ming-xian,HOU Jian.Influences of Preparation Method on Photoelectrode Performance of TiO2 Thin Films[J].Equipment Environmental Engineering,2017,14(6):17-21. |
制备方法对二氧化钛粉末薄膜光电极性能的影响研究 |
Influences of Preparation Method on Photoelectrode Performance of TiO2 Thin Films |
投稿时间:2017-04-28 修订日期:2017-06-15 |
DOI:10.7643/ issn.1672-9242.2017.06.004 |
中文关键词: 薄膜光电极 半导体粉末材料 TiO2 喷涂 光电转换效率 |
英文关键词:thin-films photoelectrode semiconductor powder material TiO2 spraying photoelectric conversion efficiency |
基金项目:国家自然科学基金项目(41576114,41376126,41676069);青岛市创新领军人才项目(15-10-3-15-(39)-zch);科技成果转化引导计划(14-2-4-4-jch) |
|
Author | Institution |
LI Heng-te | 1.Key Laboratory of Marine Corrosion and Bio-fouling, IOCAS, Qingdao 266000, China; 2.University of Chinese Academy of Sciences, Beijing 100049, China |
LIU Xing-chen | 1.Key Laboratory of Marine Corrosion and Bio-fouling, IOCAS, Qingdao 266000, China; 2.University of Chinese Academy of Sciences, Beijing 100049, China |
JING Jiang-ping | 1.Key Laboratory of Marine Corrosion and Bio-fouling, IOCAS, Qingdao 266000, China; 2.University of Chinese Academy of Sciences, Beijing 100049, China |
SUN Meng-meng | Key Laboratory of Marine Corrosion and Bio-fouling, IOCAS, Qingdao 266000, China |
CHEN Zhuo-yuan | Key Laboratory of Marine Corrosion and Bio-fouling, IOCAS, Qingdao 266000, China |
SUN Ming-xian | State Key Laboratory for Marine Corrosion and Protection, Luoyang Ship Material Research Institute (LSMRI), Qingdao 266101, China |
HOU Jian | State Key Laboratory for Marine Corrosion and Protection, Luoyang Ship Material Research Institute (LSMRI), Qingdao 266101, China |
|
摘要点击次数: |
全文下载次数: |
中文摘要: |
目的 研究光电功能涂层制备方法对粉末薄膜光电极的光电转换效率的影响。方法 采用喷涂法制备光电材料的FTO薄膜光电极,观察其表面形貌,通过研究光电流和光电位的变化评价光电材料的光电转换效率,并与点涂法和电泳法制备的光电极进行对比分析。结果 喷涂法制备的二氧化钛FTO薄膜光电极性能优于其他两种方法制备的电极,在3.5%氯化钠溶液中,光电位变化更稳定,压降大于500 mV,光电流变化大于60 μA/cm2。结论 喷涂法制备光电极能够提高半导体粉末材料的光电化学效率,是一种可推行的薄膜光电极制备方法。 |
英文摘要: |
Objective To study influences of preparation method of photoelectric functional coating on photoelectric conversion efficiency of TiO2 thin films. Methods The FTO thin film photoelectrodes were prepared by spraying. Based on observation of surface appearance, the photoelectric conversion efficiency of photoelectric materials was estimated by studying changes of light current and photopotential and compared with photoelectrode prepared by spot coating and electrophoresis. Results The TiO2 FTO thin-film prepared by spraying has better performance than electrode prepared with the other two methods. In 3.5% NaClsolution, the photoelectricity change was more stable, the pressure drop was larger than 500 mV and the light current changed by more than 60 μA/cm2. Conclusion Preparing photoelectrode by spraying could improve the photoelectrochemical efficiency of the semiconductor powder material. It is a thin film photoelectrode preparation method which could be practiced. |