潘峤,张骐,王璐,张兴华,刘明,孙志华,高蒙,高建.三种可磨耗封严涂层的抗腐蚀性能[J].装备环境工程,2017,14(6):93-96. PAN Qiao,ZHANG Qi,WANG Lu,ZHANG Xing-hua,LIU Ming,SUN Zhi-hua,GAO Meng,GAO Jian.Corrosion Resistance of Three Kinds of Abradable Seal Coatings[J].Equipment Environmental Engineering,2017,14(6):93-96. |
三种可磨耗封严涂层的抗腐蚀性能 |
Corrosion Resistance of Three Kinds of Abradable Seal Coatings |
投稿时间:2017-04-11 修订日期:2017-06-15 |
DOI:10.7643/ issn.1672-9242.2017.06.018 |
中文关键词: 可磨耗涂层 抗腐蚀 盐雾 湿热 |
英文关键词:abradable seal coating corrosion resistance salt spray thermal-humidity |
基金项目: |
|
Author | Institution |
PAN Qiao | Key Laboratory of Science and Technology on Advanced Corrosion and Protection for Aviation Material, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China |
ZHANG Qi | Key Laboratory of Science and Technology on Advanced Corrosion and Protection for Aviation Material, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China |
WANG Lu | AECC Liming Aero-engine Corporation, Shenyang 110043, China |
ZHANG Xing-hua | Key Laboratory of Science and Technology on Advanced Corrosion and Protection for Aviation Material, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China |
LIU Ming | Key Laboratory of Science and Technology on Advanced Corrosion and Protection for Aviation Material, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China |
SUN Zhi-hua | Key Laboratory of Science and Technology on Advanced Corrosion and Protection for Aviation Material, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China |
GAO Meng | Key Laboratory of Science and Technology on Advanced Corrosion and Protection for Aviation Material, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China |
GAO Jian | Key Laboratory of Science and Technology on Advanced Corrosion and Protection for Aviation Material, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China |
|
摘要点击次数: |
全文下载次数: |
中文摘要: |
目的 研究AHБ,CuAl/NiC和NiCrAl/NiC三种可磨耗涂层的抗腐蚀性能。方法 对三种涂层试样进行盐雾试验、湿热试验和浸泡试验,并结合电化学测试分析不同涂层试样的抗腐蚀性能。结果 545 h的盐雾试验后,AHБ涂层的表面出现了一处微裂纹,CuAl/NiC涂层表明出现了涂层剥落现象,NiCrAl/NiC涂层的表面状况相对最好;三种涂层试样经过10个循环的湿热试验后均未见明显的腐蚀现象;经过15 d的浸泡试验后,NiCrAl/NiC涂层的表面状况相对较好,而AHБ涂层和CuAl/NiC涂层的表面状况相对较差;电化学测试结果也表明NiCrAl/NiC涂层的防护性能相对最好。结论 NiCrAl/NiC涂层的抗腐蚀性能相对较高,而AHБ涂层和CuAl/NiC涂层的抗腐蚀性能相对较低。 |
英文摘要: |
Objective To research the corrosion resistance of three kinds of abradable seal coatings, including AHБ, CuAl/NiC and NiCrAl/NiC. Methods The corrosion resistance of the three kinds of coatings was analyzed by salt spray test, thermal-humidity test and immersion test, in combination with electrochemical testing. Results After salt spray test of 545 hours, NiCrAl/NiC coating revealed a relatively better property compared to that of AHБ and CuAl/NiC since a macro crack was found on AHБ coating and coating pill-off happened on CuAl/NiC; no obvious change was found during 10 days’ thermal-humidity test; while after 15 days’ immersion test, NiCrAl/NiC coating still showed a more stable situation than the other two coatings; the electrochemical results also provided a reliable evidence that NiCrAl/NiC had the best corrosion resistance among those three kinds. Conclusion The NiCrAl/NiC coating has relatively better corrosion resistance compared to that of AHБ and CuAl/NiC coatings. |