刘成臣,张洪彬,赵连红,金涛,王浩伟.机载电子设备灌封材料在西沙环境下的耐老化性研究[J].装备环境工程,2017,14(8):95-98. LIU Cheng-chen,ZHANG Hong-bin,ZHAO Lian-hong,JIN Tao,WANG Hao-wei.Aging Resistance of Airborne Electronic Equipment Potting Materials in Xisha Environment[J].Equipment Environmental Engineering,2017,14(8):95-98. |
机载电子设备灌封材料在西沙环境下的耐老化性研究 |
Aging Resistance of Airborne Electronic Equipment Potting Materials in Xisha Environment |
投稿时间:2017-03-14 修订日期:2017-08-15 |
DOI:10.7643/issn.1672-9242.2017.08.018 |
中文关键词: 灌封材料 西沙环境 暴露试验 老化性能 |
英文关键词:potting material Xisha environment exposure test aging performance |
基金项目: |
|
Author | Institution |
LIU Cheng-chen | Aviation Key Laboratory of Science and Technology on Structural Corrosion Prevention and Control, China Special Vehicle Research Institute, Jingmen 448035, China |
ZHANG Hong-bin | China Electronic Product Reliability and Environmental Testing Institute, Guangzhou 440106, China |
ZHAO Lian-hong | Aviation Key Laboratory of Science and Technology on Structural Corrosion Prevention and Control, China Special Vehicle Research Institute, Jingmen 448035, China |
JIN Tao | Aviation Key Laboratory of Science and Technology on Structural Corrosion Prevention and Control, China Special Vehicle Research Institute, Jingmen 448035, China |
WANG Hao-wei | Aviation Key Laboratory of Science and Technology on Structural Corrosion Prevention and Control, China Special Vehicle Research Institute, Jingmen 448035, China |
|
摘要点击次数: |
全文下载次数: |
中文摘要: |
目的 考察机载电子设备常用灌封材料在西沙环境下的耐老化性能。方法 开展西沙海洋环境下4种灌封材料的棚下暴露实验,暴晒实验时间为3年,分别通过测试表面电阻、体积电阻、介电常数、损耗角正切等手段研究其老化特点。结果 267有机硅、DC160有机硅两类样品外观未出现明显变化,且介电常数、损耗角正切、表面电阻、体积电阻均变化较小,112FR环氧树脂、8836聚氨酯两类样品出现变色、产生针孔起泡等现象,介电常数、损耗角正切、表面电阻和体积电阻均变化幅度较大。结论 在机载电子设备选用绝缘灌封材料时,可优先选用267有机硅、DC160有机硅这两类灌封材料,112FR环氧树脂和8836聚氨酯谨慎选用。 |
英文摘要: |
Objective To investigate the aging resistance of commonly used potting materials for airborne electronic equipment in Xisha environment. Methods The experiment was carried out on four kinds of potting materials by exposing them for 3 years in the Xisha marine environment. Their aging characteristics were studied by testing the surface resistance, the volume resistance, the dielectric constant, the loss tangent, etc. Results Samples of 267 silicone, DC160 silicone did not show significant changes in the appearance. Their dielectric constant, loss tangent, surface resistance, volume resistance changed slightly. Samples of 112FR epoxy resin and 8836 polyurethane appeared discoloration, pinhole foaming and other phenomena. Their dielectric constant, loss tangent, surface resistance and volume resistance changed greatly. Conclusion In selection of insulating potting material for airborne electronic equipment, 267 silicone, DC160 silicone might be given preference; 112FR epoxy resin and 8836 polyurethane should be selected carefully. |