| 刘泉兵,陈法锦,胡杰珍,邓培昌,王贵,罗思维.热带海洋大气环境下X70管线钢的缝隙腐蚀行为研究[J].装备环境工程,2017,14(9):57-62. LIU Quan-bing,CHEN Fa-jin,HU Jie-zhen,DENG Pei-chang,WANG Gui,LUO Si-wei.Crevice Corrosion Behaviors of X70 Pipeline Steel in Tropic Marine Atmosphere[J].Equipment Environmental Engineering,2017,14(9):57-62. |
| 热带海洋大气环境下X70管线钢的缝隙腐蚀行为研究 |
| Crevice Corrosion Behaviors of X70 Pipeline Steel in Tropic Marine Atmosphere |
| 投稿时间：2017-07-17 修订日期：2017-09-15 |
| DOI：10.7643/ issn.1672-9242.2017.09.012 |
| 中文关键词: 热带海洋大气 X70管线钢 缝隙腐蚀 风速 Cl-沉降速率 |
| 英文关键词:tropic marine atmosphere X70 pipeline steel crevice corrosion wind speed sedimentation rate of the Cl- |
| 基金项目:广东省自然科学基金（2015A030313619）；广东省省级科技计划项目（2016A020225004）；湛江市科技计划项目（2015A02024） |
|
|
| Author | Institution |
| LIU Quan-bing | Guangdong Ocean University a. College of Oceanography and Meteorology, Zhanjiang 524088, China |
| CHEN Fa-jin | Guangdong Ocean University a. College of Oceanography and Meteorology, Zhanjiang 524088, China |
| HU Jie-zhen | Guangdong Ocean University b.The Key Lab of Corrosion and Protection of Engineering Materials and Equipment in the Marine Environment of Zhanjiang, Zhanjiang 524088, China |
| DENG Pei-chang | Guangdong Ocean University c.College of Chemistry and Environment, Zhanjiang 524088, China |
| WANG Gui | Guangdong Ocean University b.The Key Lab of Corrosion and Protection of Engineering Materials and Equipment in the Marine Environment of Zhanjiang, Zhanjiang 524088, China |
| LUO Si-wei | Guangdong Ocean University d.College of Mechanical and Power Engineering, Zhanjiang 524088, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 研究X70管线钢在热带海洋大气实海环境下的缝隙腐蚀行为。方法 在距离湛江东海岛海岸50 m和200 m处分别搭建楔型缝隙模型，安装大气环境Cl-收集装置和自动气象监测站。结果 距离海岸越近，风速越大，大气中Cl-沉降速率也越大，X70管线钢缝隙腐蚀越严重。X70管线钢在距离海岸50 m处发生缝隙腐蚀的最大缝宽约为0.96 mm，200 m处最大缝宽约为3.75 mm，50 m处缝隙腐蚀更严重。结论 缝隙腐蚀区域形成了氧浓差电池，同时随着缝隙液中Cl-向缝隙内迁移，发生闭塞区电池自催化过程，在二者共同作用下，缝隙腐蚀区域较非缝隙腐蚀区域腐蚀更严重。 |
| 英文摘要: |
| Objective To investigate crevice corrosion behaviors of X70 pipeline steel in tropic marine atmosphere. Methods A wedge-type crevice model, Cl- -collecting device and automatic meteorological station were set up respectively 50 m and 200 m away from Donghai island of Zhanjiang. Results As close to the coast, the wind speed and the sedimentation rate of atmospheric Cl- got greater and the crevice corrosion of X70 pipeline steel was more serious. The maximal crevice width of X70 pipeline steel 50 meters and 200 meters away from the coast were respectively about 0.96 mm and 3.75 mm; the corrosion of X70 pipeline steel 50 m away from the coast was more serious. Conclusion Oxygen concentration cell forms in the area with crevice corrosion. The autocatalysis of cell generates in the occluded area as the migration of the Cl- in the liquid of the crevice gap. In the combination of the two mechanisms, the areas with crevice corrosion are more serious than other areas. |