李涛,张超,王广超,游加旺,刘元海,王浩伟.适用于DOT4制动液环境丙烯酸氨基烤漆的制备与性能研究[J].装备环境工程,2017,14(11):94-97. LI Tao,ZHANG Chao,WANG Guang-chao,YOU Jia-wang,LIU Yuan-hai,WANG Hao-wei.Preparation and Performance of Polyacrylate/Amino Resin Coating for Environment with DOT4[J].Equipment Environmental Engineering,2017,14(11):94-97. |
适用于DOT4制动液环境丙烯酸氨基烤漆的制备与性能研究 |
Preparation and Performance of Polyacrylate/Amino Resin Coating for Environment with DOT4 |
投稿时间:2017-09-16 修订日期:2017-11-15 |
DOI:10.7643/ issn.1672-9242.2017.11.019 |
中文关键词: 高酸价丙烯酸树脂 丙烯酸氨基烤漆 耐制动液 耐冲击性 |
英文关键词:polyacrylate resin with high acid value polyacrylate/amino resin coating braking-oil-resistance shock- resistance |
基金项目:国家自然科学基金(51775540);浙江省重点研发计划(2015C01SA790002);中国科学院战略性先导科技专项(XDA13040601);宁波市自然科学基金(2016A610263) |
|
Author | Institution |
LI Tao | Navy Aviation Military Representative Office in Xiangfan, Xiangyang 441000, China |
ZHANG Chao | China Special Vehicle Research Institute, Jingmen 448035, China |
WANG Guang-chao | China Special Vehicle Research Institute, Jingmen 448035, China |
YOU Jia-wang | China Special Vehicle Research Institute, Jingmen 448035, China |
LIU Yuan-hai | China Special Vehicle Research Institute, Jingmen 448035, China |
WANG Hao-wei | China Special Vehicle Research Institute, Jingmen 448035, China |
|
摘要点击次数: |
全文下载次数: |
中文摘要: |
目的 提高丙烯酸氨基烤漆的耐DOT4制动液性能,并保留其良好的耐冲击性能。方法 通过制备高酸价的丙烯酸树脂并与一定量的高分子量的环氧树脂(E20)共混改性后,与氨基树脂混合加热固化制备涂层,分别采用DOT4制动液高温浸泡法、划格法和冲击试验测涂层的耐制动液、附着力和耐冲击性能。结果 成功制备了酸价为60 mgKOH/g与固含量为60%高酸价丙烯酸树脂。当高酸价丙烯酸树脂以质量比为3:1的比例与氨基树脂混合并加入4%的E20时制备的涂层具有优异的综合性能,涂层的附着力为0级,耐冲击性能为50 kg•cm,在100 ℃的DOT4制动液中浸泡7 h后,涂层不脱落,不起泡。结论 该方法适用于提高丙烯酸氨基烤漆的耐DOT4制动液性能。 |
英文摘要: |
Objective To improve the DOT4 braking-oil-resistance of polyacrylate/amino resin coating and retain its good shock resistance. Methods Polyacrylate resin with high acid value was synthesized with high molecular weight epoxy resin (E20) to prepare polyacrylate/amino resin coating by mixing, heating and curing with the polyacrylate resin. The braking-oil-resistance, adhesive force and shock resistance of the polyacrylate/amino resin coating were tested with high temperature soaking method, grid test and shock test of DOT4. Results The polyacrylate resin with acid value of 60 mgKOH/g and solid content of 60% was synthesized successfully. When the ratio of polyacrylate resin to the amino resin equaled to 3:1 and the concentration of E20 equaled to 4% based on the sum of the mass polyacrylate resin and amino resin, the coating had the best combination property with adhesive force of 0 grade and shock resistance of 50 kg•cm. The coating could stand baking in DOT4 at 100 ℃ for 7 h without exfoliating or blistering. Conclusion This method is suitable for improving DOT4 brake fluid resistance of acrylic amino paint. |