崔明月,王青华,温宁华,李大朋,邹春梅,李慧心,张雷.哈法亚油田注水井管材腐蚀规律研究[J].装备环境工程,2018,15(6):70-73. CUI Ming-yue,WANG Qing-hua,WEN Ning-hua,LI Da-peng,ZOU Chun-mei,LI Hui-xin,ZHANG Lei.Corrosion Laws of Injection Pipe in Hafaya Oilfield[J].Equipment Environmental Engineering,2018,15(6):70-73. |
哈法亚油田注水井管材腐蚀规律研究 |
Corrosion Laws of Injection Pipe in Hafaya Oilfield |
投稿时间:2018-03-06 修订日期:2018-06-25 |
DOI:10.7643/ issn.1672-9242.2018.06.013 |
中文关键词: L80钢 注水井 腐蚀 哈法亚油田 |
英文关键词:L80 steel injection well corrosion Halfaya oilfield |
基金项目: |
|
Author | Institution |
CUI Ming-yue | Engineering Technology Center of China Petroleum Exploration and Development Research Institute, Beijing, 100083, China |
WANG Qing-hua | Engineering Technology Center of China Petroleum Exploration and Development Research Institute, Beijing, 100083, China |
WEN Ning-hua | Anke Engineering Technology Research Institute (Beijing) Co., Ltd, Beijing, 100083, China |
LI Da-peng | Anke Engineering Technology Research Institute (Beijing) Co., Ltd, Beijing, 100083, China |
ZOU Chun-mei | Engineering Technology Center of China Petroleum Exploration and Development Research Institute, Beijing, 100083, China |
LI Hui-xin | New Material Technology Research Institute, University of Science and Technology Beijing, Beijing, 100083, China |
ZHANG Lei | New Material Technology Research Institute, University of Science and Technology Beijing, Beijing, 100083, China |
|
摘要点击次数: |
全文下载次数: |
中文摘要: |
目的 合理地进行井筒选材和更好地开展防腐工作。方法 通过高压釜模拟哈法亚油田注水井腐蚀介质环境,研究温度、压力和pH对注水井油管L80钢腐蚀规律的影响。结果 随着实验温度的升高,L80钢表面腐蚀产物越来越疏松,腐蚀速率增大;随着注水压力的升高,腐蚀速率增大,局部腐蚀逐渐增强;随着pH的升高,L80的腐蚀速率有所降低,主要发生全面腐蚀;腐蚀产物主要为铁的氧化物和CaCO3。结论 该研究为井筒选材和防腐工作提供一定的技术支持。 |
英文摘要: |
Objective To reasonably select wellbore materials and carry out corrosion prevention. Methods Through the autoclave simulation Halfaya oilfield water injection corrosion environment, effects of temperature, pressure and pH on the corrosion law of L80 steel in injection well were studied. Results With the increase of the experimental temperature, the corrosion products of the sample surface were loosen, the protection ability of the samples was worsen, and the corrosion rate of the L80 pipe got higher. With the increase of injection pressure, the corrosion rate became higher, and the local corrosion was worsen. In the acid environment, with the increase of pH, the corrosion rate of L80 decreased, and the main corrosion occurred. The corrosion products are mainly iron oxide and CaCO3 scale. Conclusion The research work provides certain technical support for wellbore material selection and corrosion prevention. |