吴帅,王长鹏,苏艳,陈喜栋,张凯,赵丽旸.18CrNi4WA 钢渗碳针阀体开裂失效分析[J].装备环境工程,2018,15(7):75-79. WU Shuai,WANG Chang-peng,SU Yan,CHEN Xi-dong,ZHANG Kai,ZHAO Li-yang.Cracking Failure of Carburized Injector Valve of 18CrNi4WA Steel[J].Equipment Environmental Engineering,2018,15(7):75-79. |
18CrNi4WA 钢渗碳针阀体开裂失效分析 |
Cracking Failure of Carburized Injector Valve of 18CrNi4WA Steel |
投稿时间:2018-04-27 修订日期:2018-07-25 |
DOI:10.7643/ issn.1672-9242.2018.07.016 |
中文关键词: 针阀体 18CrNi4WA 钢 失效分析 |
英文关键词:injector valve 18CrNi4WA steel failure analysis |
基金项目: |
|
Author | Institution |
WU Shuai | Southwest Research Institute of Technology and Engineering, Chongqing 400039, China |
WANG Chang-peng | Southwest Research Institute of Technology and Engineering, Chongqing 400039, China |
SU Yan | Southwest Research Institute of Technology and Engineering, Chongqing 400039, China |
CHEN Xi-dong | Southwest Research Institute of Technology and Engineering, Chongqing 400039, China |
ZHANG Kai | Southwest Research Institute of Technology and Engineering, Chongqing 400039, China |
ZHAO Li-yang | China institute of marine technology and economy, Beijing 100081, China |
|
摘要点击次数: |
全文下载次数: |
中文摘要: |
目的 研究18CrNi4WA 钢渗碳针阀体开裂失效原因。方法 通过化学成分分析、断口扫描分析、金相组织分析、能谱分析等测试手段,对 18CrNi4WA 钢渗碳针阀体的断裂模式及失效原因进行分析。结果 针阀体失效件原始材料符合针阀体制造要求,但渗碳淬火温度过高,未得到最优的渗碳层组织,燃油中存在的硫元素导致喷油孔位置产生严重腐蚀,燃油局部压力的变化导致针阀体表面产生空蚀损伤,裂纹起始于喷油孔圆周面,自裂纹源向外发散呈月牙状,为典型疲劳断裂特征。结论 腐蚀与空蚀损伤的协同作用加快裂纹的萌生,使针阀体在热疲劳及机械振动等交变载荷的作用下产生疲劳开裂,使用寿命大为降低。 |
英文摘要: |
Objective To investigate cracking failure reasons of the carburized injector valve made of 18CrNi4WA steel. Methods The fracture modes and failure reasons of the injector valve were analyzed by means of chemical composition analysis, SEM analysis, metallographic examination and energy spectrum analysis. Results The original material of the needle valve was in conformity with the manufacturing requirement. But due to the high carburizing quenching temperature, the best carburized layer structure was not obtained. The sulfur element in fuel caused serious corrosion of injection holes. Changes of the local pressure in the fuel oil caused cavitation damage on the surface of the needle valve body. The crack began at the circumferential surface of the injection hole and radiated from the crack source to the crescent shape. It was called as typical fatigue fracture. Conclusion Synergistic effects of the corrosion and cavitation damage promote crack initiation and produces fatigue cracking under the action of the thermal-mechanics alternate fatigue load. The service life of the injector valve was greatly reduced. |