骆晨,孙志华,汤智慧,陆峰.利用薄片穿透法确定铝合金最大蚀坑深度[J].装备环境工程,2019,16(3):17-21. LUO Chen,SUN Zhi-hua,TANG Zhi-hui,LU Feng.Determination of Maximum Pit Depth of Aluminium Alloy with Foil Penetration Technique[J].Equipment Environmental Engineering,2019,16(3):17-21. |
利用薄片穿透法确定铝合金最大蚀坑深度 |
Determination of Maximum Pit Depth of Aluminium Alloy with Foil Penetration Technique |
投稿时间:2018-10-21 修订日期:2019-03-25 |
DOI:10.7643/ issn.1672-9242.2019.03.004 |
中文关键词: 铝合金 薄片穿透法 蚀坑 环境试验 |
英文关键词:aluminium alloy foil penetration technique corrosion pit environmental testing |
基金项目:国防科技工业技术基础科研项目(JSHS2016209B001) |
|
Author | Institution |
LUO Chen | Key Laboratory on Advanced Corrosion and Protection for Aviation Materials, Beijing Institute of Aeronautical Materials, AECC, Beijing 100095, China |
SUN Zhi-hua | Key Laboratory on Advanced Corrosion and Protection for Aviation Materials, Beijing Institute of Aeronautical Materials, AECC, Beijing 100095, China |
TANG Zhi-hui | Key Laboratory on Advanced Corrosion and Protection for Aviation Materials, Beijing Institute of Aeronautical Materials, AECC, Beijing 100095, China |
LU Feng | Key Laboratory on Advanced Corrosion and Protection for Aviation Materials, Beijing Institute of Aeronautical Materials, AECC, Beijing 100095, China |
|
摘要点击次数: |
全文下载次数: |
中文摘要: |
目的 研究铝合金最大蚀坑深度与环境试验时间的对应关系,为新型合金服役前的耐蚀性评级和结构件服役过程中的剩余寿命预测提供技术基础。方法 利用光学显微镜、扫描电镜分析海洋大气环境中新型铝合金的腐蚀类型,并利用薄片穿透法研究铝合金薄片最大蚀坑深度与试验时间的对应关系。结果 经过海洋大气环境暴露试验后,2A97铝合金发生了深入合金内部的严重点蚀,检测薄片试样背面电解液的出现时间,可以确定环境试验中蚀坑穿透薄片试样的时间。通过测量不同厚度薄片试样的穿透时间,可以确定最快生长局部腐蚀点的深度和时间的关系。结论 中性盐雾试验环境下,达到相同的最大蚀坑深度,2A97铝合金与AA2024铝合金用时基本相当。 |
英文摘要: |
Objective To research the relationship between maximum corrosion pit depth in aluminium alloy and environmental testing time to provide technology foundation for corrosion resistance evaluation for new alloys prior to service and life prediction of structures during service. Methods The types of corrosion of a new aluminium alloy in marine atmosphere were analyzed with optical microscopy and SEM. The relationship between maximum corrosion pit depth in aluminium alloy foil and testing time was studied with the foil penetration technique. Results Severe pitting occurred and developed deep into the 2A97 aluminium alloy substrate after exposure in marine atmosphere. Time of foil penetration during environmental testing could be determined by examination the time of appearance of electrolyte from the back of the foil. After measurement of the penetration time of foils in various thicknesses, the relationship between the depth of the fastest growing corrosion pit and time could be determined. Conclusions In neutral salt fog testing environment, it generally takes the same time for 2A97 aluminium alloy and AA2024 aluminum alloy to reach the same maximum corrosion depth. |