| 张黎黎,王跃平,陈凯锋,查小琴,王晶晶,张心悦,梁宇,亓海霞.海水淡化装置内舱碳钢防护涂层寿命预测研究[J].装备环境工程,2020,17(12):119-125. ZHANG Li-li,WANG Yue-ping,CHEN Kai-feng,ZHA Xiao-qin,WANG Jing-jing,ZHANG Xin-yue,LIANG Yu,QI Hai-xia.Life Prediction of Carbon Steel Protective Coating in Inner Compartment of Seawater Desalination Plant[J].Equipment Environmental Engineering,2020,17(12):119-125. |
| 海水淡化装置内舱碳钢防护涂层寿命预测研究 |
| Life Prediction of Carbon Steel Protective Coating in Inner Compartment of Seawater Desalination Plant |
| 投稿时间：2020-04-26 修订日期：2020-06-10 |
| DOI：10.7643/issn.1672-9242.2020.12.019 |
| 中文关键词: 海水淡化 模拟加速试验 防腐涂层 寿命预测 |
| 英文关键词:desalination simulated accelerated test anticorrosive coating life prediction |
| 基金项目:国家重点研发计划项目(2016YFC0401205) |
|
|
| Author | Institution |
| ZHANG Li-li | Xiamen Branch of Luoyang Ship Material research Institute, Xiamen 361101, China |
| WANG Yue-ping | Xiamen Branch of Luoyang Ship Material research Institute, Xiamen 361101, China |
| CHEN Kai-feng | Xiamen Branch of Luoyang Ship Material research Institute, Xiamen 361101, China;Science and Technology on Marine Corrosion and Protection Laboratory, Qingdao 266101, China |
| ZHA Xiao-qin | Luoyang Ship Material research Institute ,Luoyang 471023, China;Henan Key Laboratory of Technology and Application of Structural Materials for Ships and Marine Equipment, Luoyang 471023, China |
| WANG Jing-jing | Xiamen Branch of Luoyang Ship Material research Institute, Xiamen 361101, China;Science and Technology on Marine Corrosion and Protection Laboratory, Qingdao 266101, China |
| ZHANG Xin-yue | Xiamen Branch of Luoyang Ship Material research Institute, Xiamen 361101, China |
| LIANG Yu | Xiamen Branch of Luoyang Ship Material research Institute, Xiamen 361101, China;Science and Technology on Marine Corrosion and Protection Laboratory, Qingdao 266101, China |
| QI Hai-xia | Xiamen Branch of Luoyang Ship Material research Institute, Xiamen 361101, China;Science and Technology on Marine Corrosion and Protection Laboratory, Qingdao 266101, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 获得海水淡化装置内舱碳钢防护涂层的耐热老化寿命。方法 通过调整设备的温度及压力，模拟低温多效蒸发器半浸区工作环境，进行为期20个月的浸泡加速试验。以涂层的附着力随老化时间的变化情况、涂层颜色变化情况、涂层浸泡前后微观形貌和阻抗值为评判依据，在老化经验公式的基础上进行外推计算，进行涂层热老化寿命预测。结果 该涂料在该区域经过20个月的挂片试验，涂层表面均未出现起泡、锈蚀、开裂、脱落等失效现象；表面色差变化趋势相对稳定；干态附着力为10.9 MPa，经过20个月的测试，附着力为8.95 MPa； 0.01 Hz低频阻抗(|Z|0.01 Hz)条件下，其电化学交流阻抗值由浸泡前的1.8×108 Ω.cm2下降为浸泡后的7.9×106 Ω.cm2。涂层阻抗的数量级虽有所下降，但仍然具有较高的阻抗值，具有较好的保护性能。经过老化经验公式进行外推计算，预测海水淡化装置内舱碳钢防护涂层的热老化寿命为13.33年。结论 海水淡化装置内舱防护涂料具有长寿命热老化重防腐作用。 |
| 英文摘要: |
| The work aims to obtain the heat-resistant aging life of the carbon steel protective coating in the inner compartment of seawater desalination plant. The temperature and pressure of the equipment were adjusted to simulate the working environment of the low-temperature multi-effect evaporator. Soaking acceleration test of 20 months was conducted. The thermal aging life of the coating was predicted by extrapolating the empirical formula on the basis of the change of coating adhesion with aging time, the change of coating color, the change of coating morphology before and after soaking, and the coating impedance value. The failure phenomena such as blister, rust, cracking and peeling were not found on the coating surface after 20 months of hanging test. The variation trend of color difference of coating surface was relatively stable. The dry adhesion of the coating was 10.9 MPa, and the adhesion was 8.95 MPa after 20 months of test. Under 0.01 Hz low frequency impedance (|Z|0.01 Hz), its electrochemical impedance value changed from 1.8×108 Ω.cm2 to 7.9×106 Ω.cm2. The order of magnitude of coating impedance was decreased, but was still within the scope of effective protection. The thermal aging life of carbon steel protective coating in the inner compartment of seawater desalination plant was predicted to be 13.33 years by extrapolating the aging empirical formula. The interior protective coating of seawater desalination plant has the function of long life thermal aging and anti-corrosion. |