张宪龙,吕康源,丁兆楠,陈宇光,杨义涛,张崇宏,刘向兵,薛飞.小冲杆试验测定重离子辐照A508-3钢的硬化和脆化[J].装备环境工程,2022,19(1):45-49. ZHANG Xian-long,LYU Kang-yuan,DING Zhao-nan,CHEN Yu-guang,YANG Yi-tao,ZHANG Chong-hong,LIU Xiang-bing,XUE Fei.Determination of Hardening and Embrittlement of Heavy-ion Irradiated A508-3 Steel by Small Punch Test[J].Equipment Environmental Engineering,2022,19(1):45-49. |
小冲杆试验测定重离子辐照A508-3钢的硬化和脆化 |
Determination of Hardening and Embrittlement of Heavy-ion Irradiated A508-3 Steel by Small Punch Test |
投稿时间:2021-06-08 修订日期:2021-07-21 |
DOI:10.7643/issn.1672-9242.2022.01.007 |
中文关键词: 反应堆压力容器钢 重离子辐照 小冲杆测试 辐照硬化 辐照脆化 中图分类号:TG172 文献标识码:A 文章编号:1672-9242(2022)01-0045-05 |
英文关键词:reactor pressure vessel steel heavy-ion irradiation small punch test irradiation hardening irradiation embrittlement |
基金项目:国家重点研发计划(2017YFB0702202) |
|
Author | Institution |
ZHANG Xian-long | Institute of Modern Physics, Chinese Academy of Sciences, Lanzhou 730000, China |
LYU Kang-yuan | Institute of Modern Physics, Chinese Academy of Sciences, Lanzhou 730000, China |
DING Zhao-nan | Institute of Modern Physics, Chinese Academy of Sciences, Lanzhou 730000, China |
CHEN Yu-guang | Institute of Modern Physics, Chinese Academy of Sciences, Lanzhou 730000, China |
YANG Yi-tao | Institute of Modern Physics, Chinese Academy of Sciences, Lanzhou 730000, China |
ZHANG Chong-hong | Institute of Modern Physics, Chinese Academy of Sciences, Lanzhou 730000, China |
LIU Xiang-bing | Life Management Technology R & D Center of Suzhou Nuclear Power Research Institute Co., Ltd., Suzhou 215004, China |
XUE Fei | Life Management Technology R & D Center of Suzhou Nuclear Power Research Institute Co., Ltd., Suzhou 215004, China |
|
摘要点击次数: |
全文下载次数: |
中文摘要: |
目的 采用小冲杆测试方法测量高能重离子辐照反应堆压力容器A508-3钢的辐照硬化和脆化特性,为工况条件下反应堆压力容器寿命预测提供实验依据。方法 采用兰州重离子加速器提供的高能C6+离子通过减能装置在290 ℃条件下开展A508-3钢辐照实验,并在样品表面形成一定厚度、准均匀分布的离位损伤层。通过开展不同辐照剂量辐照样品的小冲杆测试,得到不同辐照剂量A508-3钢的小冲杆载荷-位移曲线。通过对小冲杆测试得到的载荷-位移曲线的分析,测定不同辐照剂量样品的辐照硬化和脆化特性。结果 压力容器A508-3钢辐照样品的硬化和脆化随着辐照剂量的增加逐渐增强,0.15 dpa以前呈线性增长,而后缓慢增大,约0.2 dpa时达到饱和趋势。结论 通过小冲杆测试可以得到离子辐照样品的硬化和脆化行为,A508-3钢辐照硬化和脆化行为具有一致的变化趋势。 |
英文摘要: |
The hardening and embrittlement characteristics of high-energy heavy-ions irradiated reactor pressure vessel A508-3 steel are measured by small punch test method, which provides experimental basis for the life prediction of reactor pressure vessel under working conditions. The high energy C6+ ions provided by Heavy Ion Research Facility are used to irradiate A508-3 steel at 290 ℃ by means of energy degrader, and a certain thickness of quasi-uniform damaged layer are formed on the sample surfaces. The load-displacement curves of A508-3 steel with different irradiation doses are obtained by small punch test. Through the analysis of the load-displacement curves obtained from the small punch test, the irradiation hardening and embrittlement characteristics of the samples with different irradiation doses are determined. The hardening and embrittlement of A508-3 steel increased with the increase of irradiation dose. It showed a linear increase before 0.15dpa, then increased slowly, and reached saturation at about 0.2dpa. The change trend of radiation hardening and embrittlement is consistent. |