| 杨博均,魏木孟,邓玉,范国栋,姚敬华,王晶晶.铝及铝合金在自然水环境中的腐蚀行为对比研究[J].装备环境工程,2022,19(5):106-116. YANG Bo-jun,WEI Mu-meng,DENG Yu,FAN Guo-dong,YAO Jing-hua,WANG Jing-jing.Comparative Study on Corrosion Behavior of Aluminum and Aluminum Alloy in Natural Water Environment[J].Equipment Environmental Engineering,2022,19(5):106-116. |
| 铝及铝合金在自然水环境中的腐蚀行为对比研究 |
| Comparative Study on Corrosion Behavior of Aluminum and Aluminum Alloy in Natural Water Environment |
| |
| DOI：10.7643/issn.1672-9242.2022.05.014 |
| 中文关键词: 铝合金 局部腐蚀 淡海水交替 包铝层 腐蚀速率 氯离子 电解质效应中图分类号:TG172.5 文献标识码:A 文章编号:1672-9242(2022)05-0106-11 |
| 英文关键词:aluminum alloy local corrosion freshwater-seawater alternating aluminum cladding corrosion rate chloride ion electrolyte effect |
| 基金项目: |
|
|
| Author | Institution |
| YANG Bo-jun | Xiamen Materials Research Institute, No.725 Research Institute, China Shipbuilding Industry Group Co., Ltd., Fujian Xiamen 361006, China |
| WEI Mu-meng | Xiamen Materials Research Institute, No.725 Research Institute, China Shipbuilding Industry Group Co., Ltd., Fujian Xiamen 361006, China |
| DENG Yu | Xiamen Materials Research Institute, No.725 Research Institute, China Shipbuilding Industry Group Co., Ltd., Fujian Xiamen 361006, China |
| FAN Guo-dong | Xiamen Materials Research Institute, No.725 Research Institute, China Shipbuilding Industry Group Co., Ltd., Fujian Xiamen 361006, China |
| YAO Jing-hua | Xiamen Materials Research Institute, No.725 Research Institute, China Shipbuilding Industry Group Co., Ltd., Fujian Xiamen 361006, China;State Key Laboratory for Marine Corrosion and Protection, Shandong Qingdao 266101, China |
| WANG Jing-jing | Xiamen Materials Research Institute, No.725 Research Institute, China Shipbuilding Industry Group Co., Ltd., Fujian Xiamen 361006, China;State Key Laboratory for Marine Corrosion and Protection, Shandong Qingdao 266101, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 分析研究铝及铝合金在自然水环境中的腐蚀行为。方法 通过开展LM3纯铝、5083铝、LF6M去包铝及带包铝在淡海水交替、海水及淡水自然环境下2 a的暴露试验，将3种环境下材料的腐蚀形貌、腐蚀速率进行对比。总结4种铝及铝合金材料在不同水环境下的腐蚀规律，对其腐蚀机理进行简要的探讨，并对其长周期的腐蚀行为进行预测。结果 通过对4种材料局部腐蚀协同影响因子(b)的对比可以发现，淡水环境对LM3纯铝局部腐蚀的影响最大，淡海水环境对5083铝合金局部腐蚀影响最大，淡水及淡海水环境对2种LF6M铝合金材料局部腐蚀的影响都很大。结论 5083、LF6M带包铝及去包铝，在淡海水交替自然环境下的耐蚀性能最差，LM3纯铝在淡水环境下耐蚀性能最差。 |
| 英文摘要: |
| This paper is to study the corrosion behaviors of aluminum and aluminum alloy in natural water environment. Through the 2-year exposure test of LM3 pure aluminum, 5083 aluminum, LF6M unclad aluminum and clad aluminum in natural environments of freshwater-seawater alternating, seawater and freshwater, the corrosion morphology and corrosion rate of the materials in the three environments were compared. The corrosion laws of four kinds of aluminum and aluminum alloy materials in different water environments were summarized, their corrosion mechanisms are briefly discussed, and their long-term corrosion behaviors were predicted. By comparing the synergistic influence factor (b) of local corrosion of four materials, we can find that the fresh water environment has the greatest impact on the local corrosion of LM3 pure aluminum; the fresh seawater environment has the greatest impact on the local corrosion of 5083 aluminum alloy; and both fresh water and fresh seawater environments have a great impact on the local corrosion of the two LF6M aluminum alloy materials. The 5083 aluminum alloy, LF6M unclad aluminum and clad aluminum have the worst corrosion resistance in freshwater-seawater alternating natural environment; and LM3 pure aluminum has the worst corrosion resistance in freshwater. |
| 查看全文 查看/发表评论 下载PDF阅读器 |