李茜,胡涛,孙茂钧,王玲,牟献良,李昊瑜,何德洪,任雁,任京,肖林林,杨立昆.基于自然和模拟热带海洋大气环境中涂层性能变化的对比研究[J].装备环境工程,2023,20(11):149-157. LI Qian,HU Tao,SUN Mao-jun,WANG Ling,MOUXian-liang,LI Hao-yu,HE De-hong,REN Yan,REN Jing,XIAO Lin-lin,YANG Li-kun.Comparative Study on Coating Performance Changes in Natural and Simulated Tropical Marine Atmospheric Environments[J].Equipment Environmental Engineering,2023,20(11):149-157. |
基于自然和模拟热带海洋大气环境中涂层性能变化的对比研究 |
Comparative Study on Coating Performance Changes in Natural and Simulated Tropical Marine Atmospheric Environments |
投稿时间:2023-05-05 修订日期:2023-06-13 |
DOI:10.7643/issn.1672-9242.2023.11.019 |
中文关键词: 涂层 热带海洋大气 自然暴露 实验室模拟 腐蚀行为 相关性中图分类号:TJ07 文献标识码:A 文章编号:1672-9242(2023)11-0149-09 |
英文关键词:coating tropical marine atmosphere natural exposure laboratory simulation corrosion behavior correlation |
基金项目: |
|
Author | Institution |
LI Qian | Southwest Institute of Technology and Engineering, Chongqing 400039, China |
HU Tao | Southwest Institute of Technology and Engineering, Chongqing 400039, China |
SUN Mao-jun | Southwest Institute of Technology and Engineering, Chongqing 400039, China |
WANG Ling | Southwest Institute of Technology and Engineering, Chongqing 400039, China |
MOUXian-liang | Southwest Institute of Technology and Engineering, Chongqing 400039, China |
LI Hao-yu | Southwest Institute of Technology and Engineering, Chongqing 400039, China |
HE De-hong | Jiangjin Atmospheric Material CorrosionField National Observation and Research Station, chognqing 402260, China |
REN Yan | Beijing North Vehicle Group Corporation, Beijing 100072, China |
REN Jing | China North Industries Corp.Beijing 100053, China |
XIAO Lin-lin | Beijing North Vehicle Group Corporation, Beijing 100072, China |
YANG Li-kun | China North Industries Corp.Beijing 100053, China |
|
摘要点击次数: |
全文下载次数: |
中文摘要: |
目的 研究涂层在自然环境试验和实验室模拟环境试验下性能的变化情况,通过再现涂层在自然环境下的环境效应和损伤过程,进而验证该模拟热带海洋大气环境试验方法的合理性。方法 根据涂层在舰船、舰载机等装备上热带海洋大气实际服役环境的分析,通过对热带海洋大气环境温度、湿度、盐雾、太阳辐射环境因素的组合,综合设计模拟热带海洋大气环境试验方法的试验流程,开展3种涂层在海南万宁为期1 a和实验室总周期为7循环的对比试验。结果 3种涂层在自然环境试验和实验室模拟环境试验后,随着试验时间的延长,其性能变化趋势相似,失光率和色差增大,附着力明显降低,交流阻抗值减小。红外光谱分析显示,老化机理均未出现明显变化,以光泽和色差为基准的平均秩相关系数为0.87,为极强相关。结论 本模拟热带海洋大气环境试验方法设计合理,具有良好的模拟性。 |
英文摘要: |
The work aims to study the performance changes of coatings in natural and simulated tropical marine atmospheric environments, to verify the rationality of the method for simulating marine atmospheric environment by reproducing the environmental effects and damage processes of coatings in natural environments. Based on the analysis of the coating on ships, carrier based aircraft, and other equipment in the tropical ocean atmosphere, and in combination with environmental factors such as temperature, humidity, salt mist, and solar radiation in the tropical marine atmosphere, a comprehensive experimental process was designed to simulate the tropical ocean atmosphere environment in the laboratory. A comparative test of three coatings in Wanning, Hainan for a period of one year and a total laboratory cycle of seven cycles was conducted. According to the test of three coatings in the natural environment and the simulated environment in laboratory, the performance changes of coatings showed a similar trend. The loss of light and color difference increased, the adhesion significantly decreased, and the AC impedance value decreased. The infrared spectroscopy analysis showed no significant change in the aging mechanism. The average rank correlation coefficient based on gloss and color difference was 0.87, which is highly correlated. The experimental method for simulating tropical marine atmospheric environment is reasonable in design and has good simulation performance. |