| Corrosion of Carbon Steel and Low-alloy Steel Exposure in Xiamen Natural Seawater |
| Received:September 10, 2012 Revised:December 15, 2012 |
| View Full Text View/Add Comment Download reader |
| DOI： |
| KeyWord:carbon steel low-alloy steel seawater exposure |
| Author | Institution |
| CHEN Xiang-feng |
1. State Key Laboratory for Marine Corrosion and Protection， Qingdao ， China;2. Xiamen Branch of Luoyang Ship Material Research Institute， Xiamen ， China |
| MU Zhen-jun |
Xiamen Branch of Luoyang Ship Material Research Institute， Xiamen ， China |
| XU Chun-sheng |
Xiamen Branch of Luoyang Ship Material Research Institute， Xiamen ， China |
| REN Run-tao |
1. State Key Laboratory for Marine Corrosion and Protection， Qingdao ， China;2. Xiamen Branch of Luoyang Ship Material Research Institute， Xiamen ， China |
| HUANG Ting |
1. State Key Laboratory for Marine Corrosion and Protection， Qingdao ， China;2. Xiamen Branch of Luoyang Ship Material Research Institute， Xiamen ， China |
| YAO Jing-hua |
1. State Key Laboratory for Marine Corrosion and Protection， Qingdao ， China;2. Xiamen Branch of Luoyang Ship Material Research Institute， Xiamen ， China |
|
| Hits: |
| Download times: |
| Abstract: |
| 2 kinds of typical carbon steel and low alloy steel were exposed in 3 zones of seawater at Xiamen for 8 a. The regulations of corrosion of two kinds of material in immersion zone, mean-tide zone and splash zone were summarized, and the long-term corrosion behavior was also predicted. |