| CAO Gong-wang,WANG Zhen-yao,WANG Chuan,LIU Yan-jie.Research on Atmospheric Corrosion of No.45 Carbon Steel in Xishuangbanna Area.Equipment Environmental Engineering,,(): |
| Research on Atmospheric Corrosion of No.45 Carbon Steel in Xishuangbanna Area |
| 投稿时间：2013-12-16 修订日期：2014-01-18 |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| DOI：10.7643/issn.1672-9242.2014.02.001 |
| KeyWord:No.45 Carbon Steel Xishuangbanna atmospheric corrosion |
| Author | Institution |
| CAO Gong-wang |
State Key Laboratory for Corrosion and Protection， Institute of Metal Research，Chinese Academy of Sciences， Shenyang ， China |
| WANG Zhen-yao |
State Key Laboratory for Corrosion and Protection， Institute of Metal Research，Chinese Academy of Sciences， Shenyang ， China |
| WANG Chuan |
State Key Laboratory for Corrosion and Protection， Institute of Metal Research，Chinese Academy of Sciences， Shenyang ， China |
| LIU Yan-jie |
State Key Laboratory for Corrosion and Protection， Institute of Metal Research，Chinese Academy of Sciences， Shenyang ， China |
|
| 摘要点击次数: |
| 全文下载次数: |
| Abstract: |
| Objective To investigate the initial-stage corrosion behavior of material exposed to the atmosphere of Xishuangbanna. Methods Several methods including weight loss analysis, SEM, XRD and FTIR were used to study the corrosion rate and corrosion products of No.45 Carbon Steel exposed to the atmosphere in Xishuangbanna for 1 year. Results In the initial stage of corrosion, the main corrosion products were γ-FeOOH, Fe(OH)3 and Fe3O4，together with a small amount of α-FeOOH. Conclusion The results showed that the corrosion level of Xishuangbanna atmospheric environment was C2. The chemical stability of rust layer gradually increased with the time, which then strengthened the protection function of the rust layer for the substrate. |